An overview of the Metal Injection Molding process

An overview of the Metal Injection Moulding process


A simple concept, a complex process



The idea to plastify powdered raw materials with the help of thermoplastic additives and subsequently use injection moulding to form complex components was first developed for ceramic components.


In the 1970s this process was developed to allow the processing of metal powders by Raymond Wiech in the US, widely considered the inventor of the Metal Injection Molding process. 


The principal technological problems that had to be solved before the MIM process could be industrialised included:


Production of a homogeneous powder-binder mix with a high metal powder loading and sufficient viscosity for injection moulding


Development of economical binder removal processes providing shape retention


Sintering to high density and ensuring high dimensional accuracy.




1: Preparing the feedstock



The primary raw materials Metal Injection Molding are metal powders and a thermoplastic binder. The binder is only an intermediate processing aid and must be removed from the products after injection moulding. The properties of the powder determine the final properties of the Metal Injection Molded product.


The blended powder mix is worked into the plastified binder at an elevated temperature using a kneader or shear roll extruder. The intermediate product is the so-called feedstock. It is usually granulated with granule sizes of several millimetres, as is common in the plastic injection moulding industry.


Feedstock can either be purchased “ready to mould” from a number of international suppliers, or it can be manufactured in-house by a MIM producer if the necessary skills and knowledge are available.




2: Injection moulding



The ‘green’ MIM parts are formed in an injection moulding process equivalent to the forming of plastic parts. The variety of part geometries that can be produced by this process is similar to the great variety of plastic components.




3: Binder removal



The subsequent binder removal process serves to obtain parts with an interconnected pore network without destroying the shape of the components. The types of binder removal processes applied are further explained later in this introduction.


At the end of the binder removal process there is often still some binder present in the parts holding the metal powder particles together, but the pore network allows the evaporation of the residual binder quickly in the initial phase of sintering, at the same time as sintering necks start to grow between the metallic particles.




4: Sintering



The sintering process leads to the elimination of most of the pore volume formerly occupied by the binder. As a consequence, MIM parts exhibit a substantial shrinkage during sintering. The linear shrinkage is usually as high as 15 to 20%.


If required, sintered MIM parts may be further processed by conventional metalworking processes such as heat treatments or surface treatments in the same way as cast or wrought parts.


For certain applications, such as the automotive, medical and aerospace sectors, Hot Isostatic Pressing (HIP) can be used to completely remove any residual porosity. As MIM parts are typically small, this can be relatively cost effective for critical components.


CATEGORIES

LATEST NEWS

CONTACT US

Contact: Alexander Sun

Phone: +86 19916725893

Tel: 0512-55128901

Email: [email protected]

Add: No.6 Huxiang Road, Kunshan development Zone, Jiangsu
Shanghai Branch: No. 398 Guiyang Rd, Yangpu District, Shanghai, China